ultrasonic metal welding

Ultrasonic metal welding is local and limited to the shear forces and displacement of intermediate layers. A longer welding time results in a more even welded connection, higher yield limit and higher fracture strengths. During ultrasonic metal welding, a complex process is triggered involving static forces, oscillating shearing forces and a moderate temperature increase in the welding area. The magnitude of these factors depends on the thickness of the workpieces, their surface structure, and their mechanical properties. The workpieces are placed between a fixed machine part, i.e. the anvil, and the sonotrode, which oscillates horizontally during the welding process at high frequency (usually 20 or 35 or 40 kHz) (figure 1). The most commonly used frequency of oscillation (working frequency) is 20 kHz. This frequency is above that audible to the human ear and also permits the best possible use of energy. For welding processes which require only a small amount of energy, a working frequency of 35 or 40 kHz may be used. The static pressure is introduced at right angles to the welding interface. Here, the pressure force is superimposed by the high-frequency oscillating shearing force. As long as the forces inside the workpieces are below the limit of linear elasticity, the pieces will not deform. If forces surpass a given threshold value, local material deformation will soon take place.

These shearing forces, at high frequency, break down contamination, remove it and produce a bond between pure metal interface. The further oscillation makes the interface deformation grow until a large welding area has been produced. At the same time, there is an atomic diffusion in the contact area and the metal re-crystallizes into a fine grain structure having the properties of a cold-worked metal. Ultrasonic metal welding is local and limited to the shear forces and displacement of intermediate layers. However, a fusion does not take place if the pressure force, the amplitude and the welding time have been properly adjusted. Microscopic analyses using optical and electronic microscopes make re-crystallization, diffusion and other metallurgical phenomena evident. However, they provide no evidence of fusion (melted interface). The use of highly sensitive thermal sensing devices in the intermediate layers shows in an initial quick rise

A longer welding time results in a more even welded connection, higher yield limit and higher fracture strengths. Accordingly the metal fatigue characteristics of the welded specimens with longer welding time are improved. The research results were used for aluminum and copper plate welding. Using ultrasonic energy it is possible to weld several elements at one time. Ultrasonics complex vibrations with two- or three-dimensional vibration locus are effective for various applications. Complex vibration systems using a longitudinal-torsional vibration converter with diagonally slitted parts and a complex transverse vibration source driven by multiple longitudinal driving systems have been proposed and studied. Applications of the complex vibration systems include ultrasonic direct welding of LSI, semiconductor chips without any adhesive and solder, ultrasonic seam welding of aluminum, copper plates for heat exchanger or heat sink, ultrasonic welding of thick metal specimens such as an automobile body, etc.

                  

 <<Previous Page of Mech seminar      Mechanical Seminar Continues >>

Also See

Mechanical Engineering Projects

Energy Science & Engineering Seminar Topics for Mechanical Engineering (new)

Mechatronics Engineering Seminar Topics

Latest Mechanical Engineering Seminar Topics 2014 (new)

Automobile Related Seminar Topics for Mechanical Engineering (new)

M.tech Seminar Presentations for Mechanical Engineering (new)

Technical Seminar Papers for Mechanical Engineering (new)

Download Mechanical Engineering Seminar Topics Free